1. Gold nanorods stabilized with cetyltrimethylammonium bromide
        (CTAB)  
[a] Product name: [CTAB-AuNRs]
Manufacturing procedure: Seed mediated method
CTAB concentration: 200 mM
Longitudinal Surface Plasmon Resonance (LSPR): 748 nm
Transverse Surface Plasmon Resonance (TSPR): 513 nm
Particle shape: rod
Length = 35.3 nm
Diameter = 8.6 nm
Average Aspect Ratio: ±4.1 nm
Surface Charge = -38.5 mV
















 
2. Functionalization of  gold nanorods (AuNRs)
[a] Product name: [MUDA-AuNRs]  (MUDA = 11-mercapto-undecanoic acid)
Manufacturing procedure: Ligand exchange method
MUDA concentration: 200 mM
Longitudinal Surface Plasmon Resonance (LSPR): 738 nm
Transverse Surface Plasmon Resonance (TSPR): 515 nm
Particle shape: rod
Average Aspect Ratio: ±4 nm
Surface Charge = -57 mV


















[b] Product name: [PEG-AuNRs] (PEG = HO-PEG-SH)
Manufacturing procedure: Ligand exchange method
PEG concentration: 16.6 mg/ml
Longitudinal Surface Plasmon Resonance (LSPR): 725 nm
Transverse Surface Plasmon Resonance (TSPR): 524 nm
Particle shape: rod
Average Aspect Ratio: ±4 nm
Surface Charge = -19 mV







 